Plastics

Plastics are organic materials made from large molecules that are constructed by a chain-like attachment of certain building block molecules. The different types of plastics can be broken up into two broad categories; thermosetting plastics and thermoplastics.

 

 

 

Plastics have generic names like polypropylene, but specific products go by a plethora of brand names which are neither descriptive nor related to their generic names. It is important to know that plastics data varies from manufacturer to manufacturer, from batch to batch and even within a batch. For this reason one must be conservative when designing with plastics and refer to both the manufacturer's data sheets, test methods employed and fully understand their meaning (see Dym, 1983, Ch. 2).

 

Some Important Fundamentals

Plastics are unlike metals in several respects: they (1) yield below, at, or above their ultimate stress values, click for figure, (2) are affected by temperature, and (3) deform over time (they creep!) at significant rates, much faster than metals. For these reasons, in applications apply factors of safety to the lower value of yield or ultimate stress, seek expert advice for use other than at room temperature and, for modulus, use the Creep Modulus (also known as the Apparent Modulus) determined from creep data curves by specifying the duration of load (see Dym, 1983, p. 228).

 

Allowable Stress Values for Design

To obtain the Allowable Stress for design, apply the design for strength factor of safety FS to a Working Stress defined as the minimum of Yield vs. Ultimate Stress divided by a material factor of safety (MFS) where 3 < MFS < 5.

Example: Polypropylene Pro-fax 6523.

Data from:

a) Rubin (1990), Table 38.2, p. 441: Tensile Strength at Yield = 35.5 MPa = 5,150 psi

b) Dym (1983), table on p. 173: Tensile Strength Ultimate = 5075 psi

Choose Dym's data because it is more conservative.

Working Stress = 5075/4 = 1270 psi where MFS = 4.

Allowable Stress = 1270/1.3 = 976 psi where FS = 1.3.

This allowable tensile stress is the value used in design.

 